Pengaruh Temperatur Tempering Terhadap Kekerasan dan Ketangguhan pada Baja Karbon Sedang St60
DOI:
https://doi.org/10.38035/jgit.v1i1.14Keywords:
Absorption Energy, Hardness, Toughness, Hardening, TemperingAbstract
This study aims to determine the effect of tempering temperature on the hardness and toughness of ST60 medium carbon steel. Beginning with the hardening process aimed at increasing the natural hardness of the steel, then tempering, aimed at reducing residual stress, hardness, so that it is ductile and has toughness. The method used is an experimental approach. The object of research is hardness and toughness test specimens. Each consists of five groups; I control, II hardening, III tempering 1500C, IV tempering 3500C, and V tempering 5500C. The results of the hardness study showed an increase in hardness in the specimens of group II which had a higher hardness of 445.33 HB, group III had a hardness of 436.83 HB and IV had a hardness of 393.75 HB, while in group V there was a decrease in hardness, which had a hardness 326.41 Hb. Compared to group I which has a hardness of 380.83 HB. While the results of the toughness study showed a decrease in energy absorption in group II, namely 29.596 NM and group III, namely 33.2416 NM, while an increase in energy absorption in group IV, namely 80.8421 NM and group V 163.598 NM, compared to group I, which had an energy absorption of 50 .35N.M.
References
Anas Sudiyono. (2003). Pengantar Statistik Pendidikan. Jakarta: PT Raja Grafindo Persada.
Amanto, Hari dan Daryanto. (2003). Ilmu Bahan. Jakarta: PT Bumi Aksara..
Baumer ing, B.J.M.. (1994). Ilmu Bahan Logam Jilid I. Jakarta: PT. Bhratara Niaga Media.
Daswarman. (2012). Serial Material Teknik Dasar-Dasar Pemilihan Bahan. Jurusan Teknik Otomotif Fakultas Teknik Universitas Negeri Padang.
Direktorat Proyek Pengembangan Kurikulum. (2003). Proses Pembuatan Besi Dan Baja. Depertemen Pendidikan Nasional.
Eddy D. Hardjapamekas. (1994). Pengetahuan Bahan Dalam Penegrjaan Logam (Schonmetz. Terjemahan). Bandung: Percetakan Angkasa.
Haroen. (1984). Teknologi Untuk Bangunan Mesin Bahan-Bahan 1 (G.L.J Van Vliet. Terjemahan). Jakarta: Erlangga.
Hendri Nurdin. (2012). Perangkat Pembelajaran Teknologi Bahan. Jurusan Teknik Mesin Fakultas Teknik Universitas Negeri Padang.
Kramer, Hans dan Scharnagl, Johann. (1997). Pengetahuan Bahan Untuk Industri. Jakarta: Penebar Swadaya.
Nizam, Effendi. (2013). ‘’Studi Pengaruh Heat Input Terhadap Ketangguhan Impack Las SMAW Posisi Vertikal Baja ST60 Temper.’’(Online). Jurnal Unimus (Traksi. Vol.9. No.2.Desember). Hlm. 11. (http://jurnal.unimus.ac.id/index.php/jtm/article/view/547/ 596).
Schonmetz, Alois. dkk . (1985). Pengetahuan Bahan Dalam Pengerjaan Logam. Bandung: Angkasa (Anggota IKAPI)
Sugiyono. (2010). Metode Penelitian Kuantitatif kualitatif dan R & D. Bandung: Alfabeta.
Suharsimi Arikunto. (2006). Prosedur Penelitian. Jakarta: PT Asdi Mahasatya.
Syamsul Arifin. (1984). Ilmu Logam III. Padang: Pusat Media Pendidikan FPTK IKIP.
Tata Surdia dan Shinroku Shaito. (2005). Pengetahuan Bahan Teknik. Jakarta: PT. Pradnya Paramita.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Ebit Bimas Saputra
This work is licensed under a Creative Commons Attribution 4.0 International License.
Hak cipta :
Penulis yang mempublikasikan manuskripnya di jurnal ini menyetujui ketentuan berikut:
- Hak cipta pada setiap artikel adalah milik penulis.
- Penulis mengakui bahwa Jurnal Greenation Ilmu Teknik (JGIT) berhak menjadi yang pertama menerbitkan dengan lisensi Creative Commons Attribution 4.0 International (Attribution 4.0 International CC BY 4.0) .
- Penulis dapat mengirimkan artikel secara terpisah, mengatur distribusi non-eksklusif manuskrip yang telah diterbitkan dalam jurnal ini ke versi lain (misalnya, dikirim ke repositori institusi penulis, publikasi ke dalam buku, dll.), dengan mengakui bahwa manuskrip telah diterbitkan pertama kali di JGIT.